Enhanced ceramic material for precision alignment mechanism

ABSTRACT

Ceramics containing  80  wt % or greater of alumina (Al 2 O 3 ), with Mn, Ti, Fe, Si, Ca and Mg, with Mn—Al spinel (MnO·Al 2 O 3 ) crystals and anorthite crystals (CaO·Al 2 O 3 ·2SiO 2 ) generated by calcination, and having a volume resistivity of 1×10 11  Ω·cm or less. The ceramics contains a combined weight of 2-11 wt % or greater of Mn, Ti and Fe as the oxides, 0.5 wt % or greater of Mn as manganese dioxide (MnO 2  ), 0.5 wt % or greater of Ti as titanium oxide (TiO 2 ), and 0.5 wt % or greater of Fe as iron oxide (Fe 2 O 3 )

FIELD OF THE INVENTION

[0001] The present invention relates to a ceramic material suitable for use in a precision alignment mechanism, such as a vacuum alignment mechanism or an electrostatic alignment mechanism, for holding a glass substrate in the production of flat panel displays (“FPDs”).

BACKGROUND OF THE INVENTION

[0002] Various conventional precision alignment mechanisms or support platform have been used to support glass substrates or semiconductor wafers during the manufacture of FPDs and semiconductors. Stray light reflecting off of these conventional support devices often adversely affects the manufacturing process.

[0003] Japanese Patent Laid-Open No. 8-262090 discloses a conventional support platform on which a glass substrate for a Liquid Crystal Display (“LCD”) is mounted. The support platform is subjected to alumite processing, in which a porous layer is created on the surface of an aluminum and or aluminum alloy by anodizing treatment, and then a chemically stable surface layer is obtained by plugging or sealing that porous layer. After alumite processing, the support platform is blackened. Stray incident light is randomly reflected at the surface of the blackened support platform and absorbed, preventing undesirable halation.

[0004] Japanese Patent Laid-Open No, 8-139168 discloses a known ceramic vacuum alignment mechanism which includes a minimally-reflective thin film layer. The manufacturing trend toward ever larger FPD substrates and semiconductor wafers, however, has necessitated the production of newer ceramics alignment mechanisms with a high specific rigidity (i.e. Young's Modulus per specific gravity). Compared to aluminum (with a specific rigidity of 28 GPa·cm³/g ), Alumina ceramics or AIN ceramics have a specific rigidity of 80-95 GPa·cm³/g or 90-95 GPa·cm³/g.

[0005] Japanese Patent Laid-Open No. 2001-019540 and Japanese Patent Laid-Open No. 10-095673 disclose typical blackened ceramics alignment mechanisms with either a base of cordierite or a base of AiN, respectively. These conventional blackened ceramics require insulators, however, since electrostatic polarization occurs inside the substrate if an alignment mechanism made of these ceramics is brought into contact with an FPD substrate. Spark discharge and the substrate damage are a result of this contact.

[0006] Japanese Patent Laid-Open No. 11-245133 describes problems caused by electrostatic polarization that often occur during the manufacture of a magnetic head slider. A plurality of sliders are typically obtained by cutting a slider bar having a plurality of thin film elements formed thereon. If the slider bar is joined to an insulating jig, the electrical charge is polarized inside the metal layer of the thin film elements. Japanese Patent Laid-Open No. 11-245133 discloses using a jig of semiconductive ceramics in order to solve this problem. Surface resistivity of the disclosed jig is within a range of greater than or equal to 1×10⁶ ohms per square centimeter to less than 1×10¹² ohms per square centimeter.

[0007] Furthermore, Japanese Patent Laid-Open No. 62-094953 describes known semiconductor ceramics having a base of alumina (Al₂O₃) with 0.5-2 wt % TiO₂ added. These alumina ceramics are calcinated in a reducing atmosphere.

[0008] Japanese Patent Laid-Open No. 11-189458 discloses other conventional semiconductor ceramics having a volume resistivity of 10⁴-10¹² Ω·cm, which can withstand a voltage of 10 kV/mm or greater. These semiconductor ceramics contain alumina crystal grains of 40-85% by volume, and one or more of MnNb₂O₆, Mn₂AlO₄, or MnFe₂O4. Since alumina is relatively inexpensive and can generally be calcinated in an ordinary atmosphere, it is possible to manufacture these semiconductor ceramics on a large scale.

[0009] The object of the present invention is to provide an alumina ceramics having high specific rigidity by including a high proportion of alumina as the main component. Another object of the present invention is to provide ceramics that satisfy the requirements of low reflectance and semiconductivity, without excessively lowering the proportion of alumina.

SUMMARY OF THE INVENTION

[0010] The present invention relates to a ceramic material suitable for use in a precision alignment mechanism, such as a vacuum alignment mechanism or an electrostatic alignment mechanism, for holding a glass substrate in the production of flat panel displays (“FPDs”).

[0011] According to one aspect, the present invention is a ceramic material including at least 80 wt % of alumina with Mn, Ti, Fe, Si, Ca and Mg,with Mn -Al spinel(MnO·Al₂O₃) crystals and anorthite crystals (CaO·Al₂O₃·2SiO₂) generated by calcination, wherein volume resistivity is 1×10¹¹ Ω·cm or less.

[0012] The ceramic material further includes at least 2 wt % Mn-, Ti-or Fe-oxide, and/or at least 0.5 wt % MnO, and/or least 0.5 wt % TiO₂ and at least 0.5 wt % Fe₂O₃. The specific rigidity is at least 65 GPa·cm³/g.

[0013] Light irradiated onto a surface of the ground ceramics according to the present invention has a cumulative reflectance is 10.3-15.0% for wavelength 220-350 nm, 11.9-16.5% for wavelength 400-550 nm, and 13.8-21.7% for wavelength 600-800 nm. Alternatively, when light is irradiated onto a surface of ceramics having a surface roughness of 0.6 μRa, regular reflectance at 0 degrees is 0.6-0.9% for wavelength 220-350 nm, 0.8-1.0% for wavelength 400-550 nm, and 0.9-1.7% for wavelength 600-800 nm.

[0014] The ceramic material further includes at least 6% Si-, Ca-or Mg-oxides, and/or at least 4 wt % SiO₂, at least 0.4 wt % CaO, and at least 0.4 wt % MgO.

[0015] In a second aspect, the present invention is a ceramics manufacturing method, including the step of forming a compacted body using mixed powder containing alumina (Al₂O₃) as main components with manganese dioxide (MnO₂), titanium oxide (TiO₂), iron oxide (Fe₂O₃), silica stone or clay, dolomite, calcite and magnesite. The ceramics manufacturing method further includes the step of producing Mn-Al spinel crystals and anorthite crystals (CaO·Al₂O₃ 2SiO₂ )by calcinating the compacted body in an LPG furnace or an electrical furnace at 1,300-1,450° C.

[0016] In the following description of the preferred embodiment, reference is made to the accompanying drawings that form a part thereof, and in which is shown by way of illustration a specific embodiment in which the invention may be practiced. It is to be understood that other embodiments may be utilized and changes may be made without departing from the scope of the present invention.

BRIEF DESCRIPTION OF THE DRAWINGS

[0017] The details of the present invention, both as to its structure and operation can best be understood by referring to the following description with reference to the accompanying drawings in which:

[0018]FIG. 1 is a graph showing volume resistivity of ceramics as a function of total weight ratio of Mn, Ti and Fe;

[0019]FIG. 2 is an X-ray diffraction pattern for sample No. 5;

[0020]FIG. 3 is an X-ray diffraction pattern for sample No. 6;

[0021]FIG. 4 is an X-ray diffraction pattern for sample No. 7;

[0022]FIG. 5 is molecular maps of sample No. 5 using EPMA;

[0023]FIG. 6 is molecular maps of sample No. 7 using EPMA;

[0024]FIG. 7 shows cumulative reflectance for sample No. 1;

[0025]FIG. 8 shows cumulative reflectance for sample No. 5;

[0026]FIG. 9 shows cumulative reflectance for sample No. 6;

[0027]FIG. 10 shows cumulative reflectance for sample No. 7;

[0028]FIG. 11 shows regular reflectance for sample No. 1;

[0029]FIG. 12 shows regular reflectance for sample No. 5;

[0030]FIG. 13 shows regular reflectance for sample No. 6; and

[0031]FIG. 14 shows regular reflectance for sample No. 7.

DETAILED DESCRIPTION OF THE INVENTION

[0032] The present invention provides an alumina ceramics having high specific rigidity by including a high proportion of alumina as the main component, satisfying the requirements of low reflectance and semiconductivity, without excessively lowering the proportion of alumina.

[0033] Ceramics sintered body samples having a base of alumina (sample numbers 1 to 8) were obtained using the following process: After weighing, manganese dioxide (MnO2) powder, titanium oxide (TiO₂ ) powder, iron oxide (Fe₂O₃) powder, powdered silica stone or clay, powdered dolomite, powdered calcite and powdered magnesite are mixed with a main component of alumina (Al₂O₃) powder. A slurry is generated by wet-milling the mixed powder. The slurry is dried using a spray drying method, to generate a base powder. The base powder is press formed and calcinated at a temperature of 1,300-1,650° C. in an electrical furnace.

[0034] Ceramics for sample numbers 4 to 7 are example embodiments according to the present invention, while the ceramics of sample numbers 1 to 3 are comparative examples. Table 1 shows composition, calcination temperature, physical characteristics, volume resistivity, crystal phase, cumulative reflectance and regular reflectance for each sample.

[0035] The weight ratio of each component is shown as the oxides in Table 1. The weight ratio of Al, Ti, Fe and Mn are respectively converted to Al₂O₃, TiO₂, Fe₂O₃ and MnO. Si, Ca and Mg are respectively converted to SiO₂, CaO and MgO. Sample number 1 represents ceramics containing an extremely high proportion of alumina as a main component. The ceramics of sample numbers 1 to 3 do not contain MnO. TABLE 1 sample number 1 2 3 4 5 6 7 8 composition wt % Al₂O₃ 99.5 92.1 91.1 89.6 88.1 85.9 83.0 79.3 TiO₂ 0.0 0.0 1.1 1.1 1.1 1.5 2.0 2.7 Fe₂O₃ 0.0 0.1 0.1 1.0 2.0 2.6 3.5 5.8 MnO 0.0 0.0 0.0 0.7 1.3 1.6 2.4 3.8 SiO₂ 0.0 6.3 6.2 6.1 6.0 6.6 6.8 6.1 CaO 0.0 0.7 0.7 0.7 0.7 0.7 1.3 1.3 MgO 0.4 0.4 0.4 0.4 0.4 0.8 0.7 0.6 Na₂O 0.1 0.4 0.4 0.4 0.4 0.2 0.2 0.4 K₂O 0.0 0.0 0.0 0.0 0.0 0.0 0.1 0.0 sum 100.0 100.0 100.0 100.0 100.0 100.0 100.0 100.0 composition wt % TiO₂ + Fe₂O₃ + MnO 0.0 0.1 1.2 2.8 4.4 5.8 7.9 12.3 SiO₂ + CaO + MgO 0.4 7.3 7.3 7.2 7.1 8.1 8.8 8.0 calcination temperature° C. 1650° C. 1500° C. 1400° C. 1400° C. 1400° C. 1400° C. 1350° C. 1300° C. specific gravity GPa 3.9 3.6 3.5 3.6 3.5 3.4 3.4 3.3 young's modulus young's modulus/specific gravity 370 310 295 290 280 235 230 195 specific rigidity 94.9 86.1 85.5 81.7 80.0 69.1 68.7 59.5 volume resistivity Ω · cm 1.0E+14 8.0E+13 4.0E+13 3.0E+10 1.0E+10 4.0E+09 2.0E+08 2.0E+07 crystal phase alumina (Al₂O₃) large large large large large large large large (quantity) anorthite (CaO.Al₂O₃.2SiO₂) — small small small small small small small Mn-Al spinel (MnO.Al₂O₃) — — — very small small smaller medium medium ilmenite (FeO.TiO₂) — — — very small very small med. — — rutile (TiO₂) — — very small — — very small — — cumulative wave length of light 220 nm 40.0 22.5 22.0 12.0 11.5 10.0 reflectance % 250 nm 24.3 15.0 14.6 10.7 10.3 8.6 300 nm 38.0 14.9 14.7 10.7 10.4 8.5 350 nm 48.8 14.9 15.0 11.1 11.1 8.7 400 nm 57.8 15.8 15.6 12.1 11.9 9.5 450 nm 61.7 17.4 15.5 12.4 12.0 9.8 500 nm 67.2 20.2 15.9 13.1 12.4 10.6 550 nm 71.5 18.6 16.5 13.7 13.0 11.3 600 nm 72.3 19.7 17.1 14.1 13.8 11.8 700 nm 74.0 27.1 18.9 14.5 15.2 12.2 800 nm 72.2 29.8 21.7 14.9 17.0 12.8 regular wave length of light 220 nm 1.6 0.9 0.8 0.7 0.7 0.7 reflectance % 250 nm 1.2 0.8 0.7 0.7 0.6 0.6 300 nm 1.7 0.8 0.8 0.7 0.7 0.6 350 nm 2.2 0.9 0.9 0.8 0.8 0.7 400 nm 2.5 0.9 0.9 0.8 0.8 0.7 450 nm 2.6 1.0 0.9 0.8 0.8 0.7 500 nm 2.8 1.1 0.9 0.8 0.8 0.8 550 nm 3.1 1.1 1.0 0.9 0.9 0.8 600 nm 3.1 1.1 1.0 0.9 0.9 0.9 700 nm 3.3 1.4 1.1 1.0 1.0 0.9 800 nm 3.7 2.0 1.7 1.4 1.5 1.4

[0036] With respect to specific gravity on Table 1, about 30 mm square samples of thickness of 20 mm were prepared, and measurement was carried out using the Archimedes method. Samples of 100 mm×20 mm×2 mm were prepared, and Young's modulus was measured using a sonic test provided in JIS (Japan Industrial Standard) R 1602. Specific rigidity was calculated dividing Young's modulus by specific gravity. The ceramics have specific rigidity of 65 GPa·cm³/g or higher, so as to be able to use also with a large precision alignment mechanism or support platform. The high purity ceramics of sample number 1 has a specific rigidity of 94.9 GPa·cm³/g.

[0037] On the other hand, the ceramics of sample number 8 has a specific rigidity of 59.5 GPa·cm³/g, which is less than 70% of the specific rigidity of sample number 1 he ceramics of sample number 8 has a decreased specific rigidity, and the ceramics is required to contain 80 wt % or more of alumina.

[0038] 100 mm square samples having thickness of 20 mm were ground using a grain 140 diamond grinding wheel at upper and lower surfaces until the thickness was 6 mm. Electrodes were coated on both ends of the samples, and resistance value r was measured using an insulation ohmmeter. Volume resistivity R was obtained according to Equation (1):

R=r×S/t,  (1)

[0039] where S is surface area of the ohmmeter electrodes, and t is sample thickness.

[0040] If the ceramics for a precision alignment mechanism has a volume resistivity of 1×10¹¹ Ω·cm or less, damage to the substrate for FPD caused by electrostatic polarization is reliably prevented. The ceramics of sample numbers 4 to 8 satisfies this type of low volume resistivity. Referring to sample number 1 to 3, conductivity does not occur in ceramics that does not contain Mn. The ceramics of sample number 3 contains 1.1 wt % of Ti and 0.1 wt % of Fe, but is not semiconductive. The ceramics of sample number 4 contains 0.7 wt % of Mn. Therefore, the ceramics contains 0.5 wt % or more of Mn to appear semiconductive.

[0041] The ceramics of sample numbers 4 to 8 contain 0.5 wt % of Ti and 0.5 wt % of Fe, in addition to Mn. Also, the ceramics of sample numbers 4 to 8 contain SiO₂, CaO and MgO in a combined amount of 6-9 wt %. Referring to FIG. 1, it will be understood that if the total weight ratio of TiO₂, Fe₂O₃ and MnO becomes large, the volume resistivity becomes lower. Referring to sample numbers 2 and 3, conductivity does not appear in ceramics that contains less than a total of 2 wt % of TiO₂, Fe₂O₃ and MnO. Therefore, the alumina ceramics contain a total of 2 wt % or more of TiO₂, Fe₂O₃ and MnO to appear semiconductive.

[0042] A splinter of each sample was crushed using a mortar, and crystal analysis carried out using an X-ray diffractometer. The crystal amounts shown in Table 1 were determined based on X-ray diffraction strength. FIGS. 2, 3 and 4 show X-ray diffraction patterns for the ceramics of sample numbers 5, 6 and 7, respectively. The ceramics of sample numbers 4 to 8 were judged to be mainly composed of crystals of alumina (Al₂O₃), Mn-Al spinel (MnO·Al₂O₃) and anorthite (CaO·Al₂O₃2SiO₂). Regarding the ceramics of sample numbers 4 to 6, there are microscopic amounts of crystals composed of Ti or Fe. Crystals formed from Ti or Fe are not contained in sample numbers 7 and 8. Therefore, a lot of Ti and Fe is dissolved in the Mn-Al spinel crystals, and, as a result, conductivity is efficiently imparted using lattice imperfections inside generated non-stoichiometric compounds.

[0043] The state where oxygen is lacking at crystal interstices is called an oxygen-deficient lattice defect. The state where there is too much oxygen at crystal interstices is called an excessive oxygen, or metal deficient, lattice defect. Both types of lattice defect arise in TiO₂, which is a 3rd transition metal oxide. TiO₂ has a wide range of non-stoichiometry. A combination of oxygen-deficient lattice defects and excessive oxygen lattice defects arises in oxides of Fe, which is a 3rd transition metal. Ti and Fe, whose oxides easily form non-stoichiometric compounds, can be made to exhibit a lot of lattice defects without excessively lowering the proportion of alumina.

[0044] Splinters of sample numbers 5 and 7 were subjected to buffing using a diamond abrasive. These splinters were analyzed for each of the elements of Mg, Ca, Al, Fe, Si, Mn and Ti using electron probe microanalysis (“EMPA”). FIGS. 4 and 5 show element maps for sample No. 5 and sample No. 7, respectively. The non-uniform distribution range of Mn is at places where Mn-Al spinel crystals are generated, and overlaps with the distribution range of Fe or Ti. The non-uniform distribution range of Ca is at places where anorthite crystals are generated, and is extremely close to the distribution range of Mn, Ti and Fe. It is estimated that each component was separated by a cooling process, to produce Mn-Al spinel crystals and anorthite crystals. Alternatively, it is estimated that under the high temperature of a calcination process Mn-Al spinel crystals were produced at a molten glass interface. In either case, the production of anorthite crystals contributes to the overlapping distribution of Mn, Ti and Fe.

[0045] A 100 mm square sample (the same size as that used for measurement of volume resistivity) was used to measure optical reflectance. Light having a wavelength of 220-800 nm was irradiated to the sample surface. A cumulative reflectance was obtained by detecting light that was diffuse reflected, and regular reflectance was obtained by detecting light reflected at 0 degrees. The surface roughness of the sample was 0.6 μRa. Supposing that the cumulative reflectance of barium carbonate powder pressure compacted body is 100%, the regular reflectance of an aluminum material subjected to specular finishing was 100%. FIGS. 7 to 10 show cumulative reflectance for sample numbers 1, 5, 6 and 7 in a wavelength range of 220-800 nm, respectively. FIGS. 11 to 14 show respectively regular reflectance for the same samples, respectively. Cumulative reflectance was 10.3-15.0% for wavelength 220-350 nm, 11.9-16.5% for wavelength 400-550 nm, and 13.8-21.7% for wavelength 600-800 nm. Regular reflectance was 0.6-0.9% for wavelength 220-350 nm, 0.8-1.0% for wavelength 400 -550 nm, and 0.9-1.7% for wavelength 600-800 nm.

[0046] Table 2 shows reflectance ratios for sample numbers, for the case where reflectance of sample number 1 is 100%. From Table 2, the cumulative reflectance of sample numbers 5-8 is 18-62% of that of sample number 1. Also, the regular reflectance of sample numbers 5 to 8 is 28-67% of that of sample number 1. TABLE 2 sample number 5 6 7 8 comparison to sample No. 1 cumulative wave 220 nm 56.3% 55.0% 30.0% 28.8% reflectance % length 250 nm 61.6% 60.2% 44.2% 42.2% of light 300 nm 39.2% 38.7% 28.2% 27.5% 350 nm 30.5% 30.7% 22.8% 22.7% 400 nm 27.4% 27.0% 20.9% 20.7% 450 nm 28.2% 25.2% 20.1% 19.4% 500 nm 30.1% 23.7% 19.5% 18.5% 550 nm 26.0% 23.0% 19.2% 18.2% 600 nm 27.2% 23.7% 19.6% 19.0% 700 nm 36.6% 25.5% 19.5% 20.5% 800 nm 41.3% 30.0% 20.6% 23.6% regular wave 220 nm 56.3% 50.0% 43.8% 43.8% reflectance % length 250 nm 66.7% 61.9% 54.3% 53.9% of light 300 nm 46.8% 46.1% 40.3% 39.7% 350 nm 41.6% 40.9% 35.7% 35.3% 400 nm 36.5% 36.2% 32.2% 31.5% 450 nm 38.4% 34.3% 31.0% 30.2% 500 nm 38.7% 32.4% 29.8% 28.7% 550 nm 36.0% 31.4% 29.0% 27.9% 600 nm 35.1% 32.0% 29.1% 28.5% 700 nm 42.3% 34.3% 29.8% 30.4% 800 nm 53.4% 45.2% 38.5% 40.4%

[0047] A powders compacted body the same as that of sample numbers 6 and 7 was calcinated into ceramics using an LPG furnace instead of the electrical furnace. Table 3 shows characteristics of these ceramics, and they all have sufficiently high rigidity, low volume resistivity and low reflectance. TABLE 3 sample number 6 7 calcination temperature? 1400? 1350? specific gravity Gpa 3.4 3.4 young's modulus young's modulus/specific 232 225 specific rigidity gravity 68.2 67.2 volume resistivity Ω · cm 3.0E+09 1.0E+08 crystal phase alumina (Al₂O₃) large large (quantity) anorthite (CaO.Al₂O₃.2SiO₂) small small Mn-Al spinel (MnO.Al₂O₃) smaller medium ilmenite (FeO.TiO₂) med. — rutile (TiO₂) very small — cumulative wave length of light 220 nm 12.0 12.0 reflectance % 250 nm 10.7 10.3 300 nm 10.7 10.4 350 nm 11.1 11.1 400 nm 12.1 11.9 450 nm 12.4 12.0 500 nm 13.1 12.4 550 nm 13.7 13.0 600 nm 14.1 13.8 700 nm 14.5 15.2 800 nm 14.9 17.0 regular wave length of light 220 nm 0.7 0.6 reflectance % 250 nm 0.7 0.6 300 nm 0.7 0.7 350 nm 0.8 0.8 400 nm 0.8 0.8 450 nm 0.8 0.8 500 nm 0.8 0.8 550 nm 0.9 0.9 600 nm 0.9 0.9 700 nm 1.0 1.0 800 nm 1.4 1.5

[0048] In recent years, there has been an increase in the demand for large-scale precision alignment mechanisms or support platforms accompanying the increase in size of FPD substrates. Precision alignment mechanisms provided with large-scale bases that are expressed in units of “meters” are also known. The ceramics of the present invention can also be applied to large-scale precision alignment mechanisms or support platforms in FPD manufacturing devices and semiconductor manufacturing devices. Also, the ceramics manufacturing method of the present invention does not require a special atmosphere.

[0049] Although specific embodiments of the present invention have been described, it will be understood by those skilled in the art that there are other embodiments that are equivalent to the described embodiments. Accordingly it is to be understood that the invention is not to be limited by the specific illustrated embodiments, but only be the scope of the appended claims. 

What is claimed is:
 1. A ceramic material comprising at least 80 wt % of alumina with Mn, Ti, Fe, Si, Ca and Mg, with Mn-Al spinel (MnO-Al₂O₃) crystals and anorthite crystals (CaO·Al₂O₃ ·2SiO₂) generated by calcination, wherein volume resistivity is 1×10¹¹ Ω·cm or less.
 2. The ceramic material according to claim 1, further comprising at least 2 wt % Mn-, Ti-or Fe-oxide.
 3. The ceramic material according to claim 1, further comprising at least 0.5 wt % MnO.
 4. The ceramic material according to claim 1, further comprising at least 0.5 wt % TiO₂ and at least 0.5 wt % Fe₂O₃.
 5. The ceramic material according to claim 1, wherein specific rigidity is at least 65 GPa·cm³/g.
 6. The ceramic material according to claim 1, wherein when light is irradiated onto a surface of ground ceramics, cumulative reflectance is 10.3-15.0% for wavelength 220-350 nm, 11.9-16.5% for wavelength 400-550 nm, and 13.8-21.7% for wavelength 600-800 nm.
 7. The ceramic material according to claim 1, wherein when light is irradiated onto a surface of ceramics having a surface roughness of 0.6 μRa, regular reflectance at 0 degrees is 0.6-0.9% for wavelength 220-350 nm, 0.8-1.0% for wavelength 400-550 nm, and 0.9-1.7 for wavelength 600-800 nm.
 8. The ceramic material according to claim 1, further comprising at least 6% Si-, Ca-or Mg-oxides.
 9. The ceramic material according to claim 1, further comprising at least 4 wt % SiO₂, at least 0.4 wt % CaO, and at least 0.4 wt % MgO.
 10. A ceramics manufacturing method, comprising the steps of: forming a compacted body using mixed powder containing alumina (Al₂O₃) as main components with manganese dioxide (MnO₂ ), titanium oxide (TiO2), iron oxide (Fe₂O₃), silica stone or clay, dolomite, calcite and magnesite; and producing Mn-Al spinel crystals and anorthite crystals (CaO-Al₂O₃ 2SiO₂ )by calcinating the compacted body in an LPG furnace or an electrical furnace at 1,300-1,450° C. 